基本信息
-
双(γ-三乙氧基硅基丙基)四硫化物
-
40372-72-3
-
硅烷偶联剂KH-858;硅烷偶联剂Si-69;硅烷偶联剂KH-407;双-[3-(三乙氧基硅)丙基]-四硫化物 ;4,4’,15,15-四乙氧基-3,16-二氧杂-8,9,10,11-四硫杂-4,15-二硅杂十八烷 ;硅烷偶联剂G-407 ;双[γ-(三乙氧基硅)丙基]-四硫化物 ;4,4',15,15-四乙氧基-3,16-二氧杂-8,9,10,11-四硫杂-4,15-二硅杂十八烷 硅烷偶联剂G-407 双[Γ-(三乙氧基硅)丙基]-四硫化物;双[3-(三乙氧基硅)丙基]-四硫化物
-
C18H42O6S4Si2
-
538.94
-
3,16-Dioxa-8,9,10,11-tetrathia-4,15-disilaoctadecane,4,4,15,15-tetraethoxy-
-
254-896-5
-
1.08g/mLat 20°C(lit.)
-
3,3'-Bis(triethoxysilylpropyl)tetrasulfide; 4,4,15,15-Tetraethoxy-3,16-dioxa-8,9,10,11-tetrathia-4,15-disilaoctadecane;A 1289; B 2494; Bis(3-triethoxysilylpropyl)tetrasulfane;Bis[3-(triethoxysilyl)propyl] tetrasulfide; Bis[g-(triethoxysilyl)propyl] tetrasulfide; Cabrus 4;Degussa Si 69; EF 60; EF 60 (coupling agent); KBE 846; KBE 849; KH 845-4; KH846; MB 69; SCA 98; SIB 1825.0; Si 29; Si 69; Silane 69; Silquest A 1289;TESPT; TM 69; Unisilan 41; WD 40; WD 40 (coupling agent); Z 6940
-
91°C
-
-
250 °C
-
详细信息
偶联剂Si69-50F
偶联剂Si-69F
性能:
一面与高度分散的填料如白烟等化学反应而键结，另一面与橡胶键结，使其在硫化后产生动态及静态的优异物性。大幅减少混炼时的粘度；提高胶料的耐磨性及模数。 用量：与补强剂一起加入，白烟量的5-20%，粘土和云母粉的1.0-2.0%
用途：适用于轮胎、鞋底及滚筒、胶管、胶带、V型带等；在轮胎等橡胶制品中当耐磨剂及补强剂。
点：≥100℃
总硫含量：≥22.5%
氯含量：≤0.6%
密度：1.08-1.09g/cm3
用量：与补强剂一起加入，白烟量的 5-20%，粘土和云母
粉的 1.0-2.0%
用途：适用于轮胎、鞋底及滚筒、胶管、胶带、V 型带
等；在轮胎等橡胶制品中当耐磨剂及补强剂。